C45 Round Bar | AISI 1045 | DIN 1.1191 | JIS S45C

-
Steel C45 Round Bar is an unalloyed medium carbon steel, which is also a general carbon engineering steel. C45 is a medium strength steel with good machinability and excellent tensile properties. C45 round steel is generally supplied in the black hot rolled or occasionally in the normalised condition, with a typical tensile strength range 570 – 700 Mpa and Brinell hardness range 170 – 210 in either condition. It does not however respond satisfactorily to nitriding due to a lack of suitable alloying elements.
C45 round bar steel is equivalent to EN8 or 080M40. Steel C45 bar or plate is suitable for the manufacture of parts such as gears, bolts, general-purpose axles and shafts, keys and studs.

1. Supply Range of Steel C45 Round Bar
  • C45 Steel Round Bar: diameter 8mm – 3000mm
  • C45 Steel Plate: thickness 10mm – 1500mm  x width 200mm – 3000mm
  • C45 Steel Flat Bar: 200mm – 1000mm
  • Square C45 Steel: 20mm-800mm
  • Hexagon Steel.
Surface Finish: Black, Rough Machined, Turned or as per given requirements.
2. Common C45 Steel Specifications
CountryUSABritishJapanAustralia
StandardASTM A29EN 10083-2JIS G4051AS 1442
Grades1045C45/1.1191S45C1045
3. C45 Round Bar Steel Chemical Composition Properties
StandardGradeCMnPSSiNiCr
ASTM A2910450.43-0.500.60-0.900.040.050　-　-　-
EN 10083-2C45/1.11910.42-0.500.50-0.900.030.0350.040.40.4
JIS G4051S45C0.42-0.480.60-0.900.030.0350.15-0.35　-　-
4. Mechanical Properties of C45 Round Bar Steel Material
  • Mechanical Properties in Quenched+Tempered Condition
Diameter d (mm)Thickness t (mm)0.2 % proof stress (N/mm2)Tensile strength (N/mm2)Elongation A5 (%)Reduction Z (%)
<16<8min. 490700-850min. 14min. 35
<17-40<8<=20min. 430650-800min. 16min. 40
<41-100<20<=60min. 370630-780min. 17min. 45
Diameter d (mm)Thickness t (mm)0.2 % proof stress (N/mm2)Tensile strength (N/mm2)Elongation A5(%)
<16<16min. 390min. 620min. 14
<17-100<16<=100min. 305min. 305min. 16
<101-250<100<250min. 275min. 560min. 16
5. Forging of Carbon Steel C45 Round Bar
Hot forming temperature: 850-1200oC.
Pre heat to 750 oC – 800 oC, then continue heating to 1100 oC – 1200 oC maximum, hold until temperature is uniform throughout the section and commence forging immediately. Forging is not workable below 850 oC. Finished forgings could be air cooled.
We are strong on forged steel C45 round bar. Welcome enquiry of C45 steel materials.
6. DIN C45 Round Bar Steel Grade Heat Treatment
Forging or hot rolling:1100 – 850°C
Normalising: 840 – 880°C/air
Soft annealing: 680 – 710°C/furnace
Hardening: 820 – 860°C/water, oil
Tempering: 550 – 660°C/air
7. Hardening of DIN C45 Steel Hardening
Harden from a temperature of 820-860oC followed by water or oil quenching.
Heat to 820 oC – 850 oC hold until temperature is uniform throughout the section, soak for 10 – 15 minutes per 25mm of section, and quench in water or brine. Or,
Heat to 830 oC – 860 oC soak as above and quench in oil.Temper immediately while still hand warm.
Surface hardness for C45 special steel round bar after flame or induction hardning:
  • Steel Name       Steel number          Surface Harndess
  • C45                        1.1191                        min. 55 HRC
8. Application of DIN Carbon Steel C45 Round Bar
DIN C45 round bar steel material and steel plate C45, flats are widely used in all industry for uses which require more strength and wear resistance than the low carbon mild steel.
Quenched and subsequently tempered steel for C45 steel grade round bar, steel plate, flat and square is used for axles, bolts, forged connecting rods, crankshafts, torsion bars, light gears, guide rods, screws, forgings, wheel tyres, shafts, sickles, axes, knives, wood working drills, hammers, etc.
Welcome customers to inquiry DIN C45 round bar, CK45/1.1191 steel plate, flat steel for C45 steel price. We are professional supplier and exporter for more than 20 years. We offer you worldwide solution for C45 round bar steel.

评论

发表评论

此博客中的热门博文

AISI 8620 Steel | 1.6523 | 21NiCrMo2 | SNCM220

-
图片
AISI  8620 Steel  is a low alloy nickel, chromium, molybdenum case hardening steel, generally supplied in the as-rolled condition with a maximum hardness of HB 255max. SAE steel 8620 offers high external strength and good internal strength, making it highly wear resistant. AISI 8620 steel has a higher core strength than grades 8615 and 8617. SAE 8620 alloy steel is flexible during hardening treatments, thus enabling improvement of case/core properties. Pre-hardened and tempered (un carburized) 8620 can be further surface hardened by nitriding but will not respond satisfactorily to flame or induction hardening due to its low carbon content. Steel 8620 is suited for applications which require a combination of toughness and wear resistance. This grade is commonly supplied in round bar. 1. AISI 8620 Steel Supply Range 8620 Round Bar: diameter 8mm – 3000mm 8620 Steel Plate: thickness 10mm – 1500mm x width 200mm – 3000mm 8620 Square Bar: 20mm – 500mm 8620 tubes are also availabl
阅读全文

M2 Tool Steel | 1.3343 | HS-6-5-2C| SKH51

-
图片
M2 Tool Steel | 1.3343 | HS-6-5-2C| SKH51 AISI  M2 Tool Steel  is molybdenum based high-speed steel in tungsten–molybdenum series.  HSS  grade steel  M2  is a medium alloyed high speed steel which has good machinability. The H-SS M2 chemical composition gives a good combination of well-balanced toughness, wear resistance and red hardness properties. Widely used for cutting tools such as twist drills, taps, milling cutters, saws, knives etc. Also commonly used in cold work punches and dies and cutting applications involving high speed and light cuts. Grade M2 High Speed Steel is by far the most popular high speed steel replacing high speed steel grade  T1  in most applications because of its superior properties and relative economy. We are one of leading AISI M2 HSS steel supplier and we can offer better quality and M2 alloy steel price for your various applications. 1. Supply Range of M2  tool steel  High Speed M2 Steel Round Bar:  diameter 2mm – 200mm HSS M2 Steel Flat
阅读全文

Everything You Need To Know About Injection Molding

-
图片
What is Injection Molding: Injection Molding is a manufacturing process for producing parts in large volume. It is most typically used in mass-production processes where the same part is being created thousands or even millions of times in succession. Why Use Injection Molding: The principal advantage of injection molding is the ability to scale production en masse. Once the initial costs have been paid the price per unit during injection molded manufacturing is extremely low. The price also tends to drop drastically as more parts are produced. Other advantages include the following: Injection Molding produces low scrap rates relative to traditional manufacturing processes like CNC machining which cut away substantial percentages of an original plastic block or sheet. This however can be a negative relative to additive manufacturing processes like 3D printing that have even lower scrap rates. Note: waste plastic from injection molding manufacturing typically comes consistent
阅读全文