H13 Tool Steel | 1.2344 | X40CrMoV5-1 | SKD61 Hot Work Steel

-
H13 Tool Steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications. H13 tool steelis classified as group H steels by the AISI classification system. This series of steels start from H1 to H19.
AISI H-13 tool steel is characterized by:
  • Good resistance to abrasion at both low and high temperatures
  • High level of toughness and ductility
  • Uniform and high level of machinability and polishability
  • Good high-temperature strength and resistance to thermal fatigue
  • Excellent through-hardening properties
  • Very limited distortion during hardening
In steel H13, the molybdenum and vanadium act as strengthening agents. The chromium content assists die steel H-13 to resist softening when used at high temperatures. H-13 die steels offers an excellent combination of shock and abrasion resistance, and possesses good red hardness. It is capable of withstanding rapid cooling and resists premature heat checking. Tool Steel H13 has good machinability, good weldability, good ductility, and can be formed by conventional means.
Due to H13 tool steel excellent combination of high toughness and fatigue resistance, AISI H13 hot work tool steel is used more than any other tool steel in tooling applications.
H13 Tool Steel is a versatile chromium-molybdenum hot work steel that is widely used in hot work and cold work tooling applications. The hot hardness (hot strength) of H13 resists thermal fatigue cracking which occurs as a result of cyclic heating and cooling cycles in hot work tooling applications. Because of its excellent combination of high toughness and resistance to thermal fatigue cracking (also known as heat checking) H13 is used for more hot work tooling applications than any other tool steel.
Because of its high toughness and very good stability in heat treatment, H13 is also used in a variety of cold work tooling applications. In these applications, H13 provides better hardenability (through hardening in large section thicknesses) and better wear resistance than common alloy steels such as 4140.
Also available as Electro-Slag-Remelted (ESR) and Vacuum-Arc-Remelted (VAR) products as well. The remelting processes provide improved chemical homogeneity, refinement of carbide size, and the associated improvements in mechanical properties and fatigue properties.
APPLICATIONS: Inserts, cores, and cavities for die casting dies, die casting shot sleeves, hot forging dies, extrusion dies, and plastic mold cavities and components that require high toughness and excellent polishability.


1. Supply Range for AISI H13 Tool Steel
H13 Steel Round Bar: diameter 8mm – 400mm
H13 Steel Plate: thickness 16mm –500mm  x width 200mm – 800mm
H13 Steel Slab: 200mm x  500-800mm
Surface Finish: Black, Rough Machined, Turned or as per given requirements.
2. Common H13 Tool Steel Related Specifications
CountryUSAGermanJapan
StandardASTM A681DIN EN ISO 4957JIS G4404
GradesH131.2344/X40CrMoV5-1SKD61

3. H13 Tool Steel Chemical Composition
ASTM A681CMnPSSiCrVMo
H130.320.450.20.60.030.030.81.254.755.50.81.21.11.75
DIN ISO 4957CMnPSSiCrVMo
1.2344 /X40CrMoV5-10.350.420.250.50.030.020.81.24.85.50.851.151.11.5
JIS G4404CMnPSSiCrVMo
SKD610.350.420.250.50.030.020.81.24.85.50.81.151.01.5
 

4. AISI H13 Steel Mechanical Properties
Properties
MetricImperial
Tensile strength, ultimate (@20°C/68°F, varies with heat treatment)1200 – 1590 MPa174000 – 231000 psi
Tensile strength, yield (@20°C/68°F, varies with heat treatment)1000 – 1380 MPa145000 – 200000 psi
Reduction of area (@20°C/68°F)50.00%50.00%
Modulus of elasticity (@20°C/68°F)215 GPa31200 ksi
Poisson’s ratio0.27-0.300.27-0.30

5. Forging of H13 Tool Steel Heating for forging must be done slowly and uniformly. Soak through at 1900°-2000°F and reheat as often as necessary, stopping work when the temperature drops below 1650°F. After forging, cool slowly in lime, mica, dry ashes or furnace. H-13 should always be annealed after forging.
6. Heat Treatment for H13 Tool Steels
Heat slowly to 1550°-1650°F, hold until entire mass is heated through, and cool slowly in the furnace (40F per hour) to about 1000°F, after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
  • Stress Relieving
When desirable to relieve the strains of machining, heat slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving). Â
  • Preheat Prior to Hardening
Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.
  • Hardening
H13 tool steel is a steel having very high hardenability and should be hardened by cooling in still air. The use of a salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening in spent pitch coke is suggested. The temperature employed is usually 1800°-1850°F, depending on size section.
  • Quenching
Quench in still air or dry air blast. If complicated forms are to be hardened, an interrupted oil quench can be used. Quench part in oil and remove from bath when it just loses its color (1000°-1100°F). Finish cooling to below 150°-125°F in air, then temper immediately.
  • Tempering
Tempering practice may vary with size and application, but is usually performed in the range of maximum secondary hardness or higher. Double tempering is recommended. The results below is H13 that was air quenched from 1800°F and tempered for 4 hours at various temperatures. The results may be used as a guide, keeping in mind that parts of heavy section or mass may be several points lower in hardness.
7. Application of AISI H13 Tool Steel
  • As Tools for Extrusion
PartAluminium, mag­nesium alloys, HRCCopper al­loys HRCStainless steel HRC
Dies, Backers, die-holders, liners, dummy blocks, stems44-5043-4745-50
41-5040-4840-48
Austenitizing temperature
1,870-1,885°F1,900-1,920°F
(1,020-1,030°C)(1,040-1,050°C)
 
  • As Plastic Molding Tool Steel
PartAustenitizing temp.HRC
Injection molds Compression/ transfer molds1,870-1,885°F (1,020-1,030°C)50-52
Tempering 480°F (250°C)
 
  • Other Applications
ApplicationsAustenitizing tempHRC
Severe cold punching, scrap shears1,870-1,885°F50-52
(1,020-1,030°C)
Tempering 480°F (250°C)
Hot shearing1,870-1,885°F 
(1,020-1,030°C)50-52
Tempering 480°F (250°C) or 
1,070-1,110°F45-50
(575-600°C) 
Shrink rings (e.g. for cemented carbide dies)1,870-1,885°F45-50
(1,020-1,030°C)
Tempering 1,070-1,110°F
(575–600°C)
Wear-resisting parts1,870-1,885°FCore
50-52
Surface
~1000HV1
(1,020-1,030°C)
Tempering 1,070°F (575°C)
nitrided

If there are any queries about AISI H13 tool steel for hot working applications, please feel free to leave a comment below. And welcome enquiry of AISI H13 tool steel, we are professional and reliable supplier  for prime H13 tool steel materials.

评论

发表评论

此博客中的热门博文

What Do YOU Know About Mold Steel Quality?

-
图片
Many industries place strict requirements on the acceptable level of surface defects and imperfections that may appear on a plastic molded part. Such conditions often apply to critical components for the medical and pharmaceutical industries as well as for the manufacturers of lenses and other optical devices. However, for aesthetic reasons, many other consumer goods have similar restrictions. After all, any defect that appears on the surface of the mold steel is likely to be replicated onto the molded part. Problems associated with the texturing or polishability of a mold cavity can often be traced back to the mold steelmaking process. The material properties that have shown the greatest influence on obtaining a good surface finish are the microcleanliness level, the severity of chemical segregation and the appearance of primary carbides. The mold steel's chemical composition along with the manufacturing techniques used during its production, will determine its ability to p...
阅读全文

Everything You Need To Know About Injection Molding

-
图片
What is Injection Molding: Injection Molding is a manufacturing process for producing parts in large volume. It is most typically used in mass-production processes where the same part is being created thousands or even millions of times in succession. Why Use Injection Molding: The principal advantage of injection molding is the ability to scale production en masse. Once the initial costs have been paid the price per unit during injection molded manufacturing is extremely low. The price also tends to drop drastically as more parts are produced. Other advantages include the following: Injection Molding produces low scrap rates relative to traditional manufacturing processes like CNC machining which cut away substantial percentages of an original plastic block or sheet. This however can be a negative relative to additive manufacturing processes like 3D printing that have even lower scrap rates. Note: waste plastic from injection molding manufacturing typically comes consistent...
阅读全文

M2 Tool Steel | 1.3343 | HS-6-5-2C| SKH51

-
图片
M2 Tool Steel | 1.3343 | HS-6-5-2C| SKH51 AISI  M2 Tool Steel  is molybdenum based high-speed steel in tungsten–molybdenum series.  HSS  grade steel  M2  is a medium alloyed high speed steel which has good machinability. The H-SS M2 chemical composition gives a good combination of well-balanced toughness, wear resistance and red hardness properties. Widely used for cutting tools such as twist drills, taps, milling cutters, saws, knives etc. Also commonly used in cold work punches and dies and cutting applications involving high speed and light cuts. Grade M2 High Speed Steel is by far the most popular high speed steel replacing high speed steel grade  T1  in most applications because of its superior properties and relative economy. We are one of leading AISI M2 HSS steel supplier and we can offer better quality and M2 alloy steel price for your various applications. 1. Supply Range of M2  tool steel  High Speed M2 Ste...
阅读全文